Main Title |
Cadmium and chromium recovery from electroplating rinsewaters / |
Author |
Gavaskar, Arun R. ;
Olfenbuttel, R. F. ;
Jones, J. A. ;
Brown., L.
|
Other Authors |
|
CORP Author |
Battelle Columbus Div., OH.;Environmental Protection Agency, Cincinnati, OH. Risk Reduction Engineering Lab. |
Publisher |
U.S. Environmental Protection Agency, Risk Reduction Engineering Laboratory, |
Year Published |
1994 |
Report Number |
EPA/600/R-94/050; EPA-68-CO-0003 |
Stock Number |
PB94-160553 |
Subjects |
Electroplating ;
Cadmium ;
Chromium
|
Additional Subjects |
Materials recovery ;
Water pollution abatement ;
Electroplating ;
Cadmium ;
Chromium ;
Waste water reuse ;
Recycling ;
Economic analysis ;
Ion exchanging ;
Performance evaluation ;
Metals ;
Quality control
|
Internet Access |
|
Holdings |
Library |
Call Number |
Additional Info |
Location |
Last Modified |
Checkout Status |
NTIS |
PB94-160553 |
Some EPA libraries have a fiche copy filed under the call number shown. |
|
07/26/2022 |
|
Collation |
5 pages : illustrations ; 30 cm |
Abstract |
This evaluation addresses the product quality, pollution prevention, and economic issues involved in the use of ion exchange to recover cadmium and chromium from electroplating rinse waters. Test results showed that the water returned to the rinse after ion exchange was of acceptable quality. On the cadmium line, the ion exchange resin was regenerated with sodium hydroxide solution and the regenerant was subjected to electrolytic metal recovery to recover cadmium for reuse in the plating bath. On the chromium line, the ion exchange resin was regenerated with sodium hydroxide solution and the regenerant was passed through a cation exchange resin in an effort to recover chromic acid. However, due to excess sodium hydroxide in the regenerant, chromic acid could not be recovered with the amount of resin used. The pollution prevention potential of ion exchange on the cadmium and chromium rinse water is good, especially if further testing establishes good recovery of chromic acid. Payback periods of 1 year on the cadmium ion exchange and 8 years on the chromium system are projected. |