Bortner, M. J. AND D. G. Baird. ABSORPTION OF CO2 AND SUBSEQUENT VISCOSITY REDUCTION OF AN ACRYLONITRILE COPOLYMER. (R829555). 45(10):3399-3412, (2004).

Description:

Acrylonitrile (AN) copolymers (AN content greater than about 85 mol%) are traditionally solution processed to avoid a cyclization and crosslinking reaction that takes place at temperatures where melt processing would be feasible. It is well known that carbon dioxide (CO₂) reduces the glass transition temperature (T_g) and consequently the viscosity of many glassy and some semi-crystalline thermoplastics. However, the ability of CO₂ to act as a processing aid and permit processing of thermally unstable polymers at temperatures below the onset of thermal degradation has not been explored. This study concentrates on the ability to plasticize an AN copolymer with CO₂, which may ultimately permit melt processing at reduced temperatures. To facilitate viscosity measurements and maximize the CO₂ absorption, a relatively thermally stable, commercially produced AN copolymer containing 65 mol% AN was investigated in this research. Differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) indicated that CO₂ significantly absorbs into and reduces the T_g of the AN copolymer. Pressurized capillary rheometry indicated that the magnitude of the viscosity reduction is dependent on the amount of absorbed CO₂, which correlates directly to the T_g reduction of the plasticized material. Up to a 60% viscosity reduction was obtained over the range of shear rates tested for the plasticized copolymer containing up to 6.7 wt% CO₂ (31 °C T_g reduction), corresponding to as much as a 30 °C equivalent reduction in processing temperature. A Williams–Landel–Ferry (WLF) analysis was used to estimate the viscosity reduction based on the T_g reduction (and corresponding amount of absorbed CO₂) in the plasticized AN copolymer, and the predicted viscosity reduction based on using the universal constants was 34–85% higher than measured, depending on the amount of absorbed CO₂. Van Krevelen's empirical solubility relationships were used to calculate the expected absorbance levels of CO₂, and found to be highly dependent on the choice of constants within the statistical ranges of error of the Van Krevelen relationships.

Author Keywords: Author Keywords: Carbon dioxide; Acrylonitrile; Plasticizer

Record Details:

Record Type:DOCUMENT( JOURNAL/ PEER REVIEWED JOURNAL)

Product Published Date:01/01/2004

Record Last Revised:12/22/2005

Record ID: 85546

Show Additional Record Data

Document IDs:

EPA Number :R829555